Title: | Study of the composition of GaAs1-yBiy films obtained by pulsed laser deposition |
Authors: | Devitsky, O. V. Девицкий, О. В. Kravtsov, A. A. Кравцов, А. А. Sysoev, I. A. Сысоев, И. А. |
Keywords: | GaAs1-yBiy;Thin films;Pulsed laser deposition;Raman light scattering;Photoluminescence |
Issue Date: | 2021 |
Publisher: | TVER STATE UNIV |
Citation: | Devitsky, O. V., Kravtsov, A. A., Sysoev, I. A. Study of the composition of GaAs1-yBiy films obtained by pulsed laser deposition // PHYSICAL AND CHEMICAL ASPECTS OF THE STUDY OF CLUSTERS NANOSTRUCTURES AND NANOMATERIALS. - 2021. - Issue 13. - Page 96-105. - DOI10.26456/pcascnn/2021.13.096 |
Series/Report no.: | PHYSICAL AND CHEMICAL ASPECTS OF THE STUDY OF CLUSTERS NANOSTRUCTURES AND NANOMATERIALS |
Abstract: | Uniaxial cold pressing was used to fabricate the GaAs1-yBiy targets with the Bi content of 1 and 22 %. From the obtained targets, pulsed laser deposition of GaAs1-yBiy thin films on the GaAs and Si substrates was carried out for the first time. We studied the composition, Raman and PL spectra of thin GaAs1-yBiy films obtained from targets with 1 and 22 % of Bi. According to the photoluminescence spectra of thin GaAs1-yBiy films on GaAs substrates, it was determined that the maximum content of Bi in the films did not exceed 2,7 %. The results obtained well correlate with the results of the energy dispersive analysis, the composition of films obtained from targets with the Bi content of 1 and 22 % - GaAs0,975 Bi-0,Bi-025 and GaAs0,973Bi0,027. It was found that the LO (GaBi) phonon mode of associated with disordering during mixing of GaAs and GaBi phases to be at a frequency of 181 cm(-1). For the thin film obtained on the Si substrate, the mode LO (GaAs) was observed that was less pronounced and shifted by 3 cm(-1) to the left, while the mode TO (GaAs), forbidden by the selection rules, had a higher intensity and its shift was of about 1 cm(-1) relative to the frequency of the mode TO (GaAs) of the thin film obtained on the GaAs substrate. |
URI: | http://hdl.handle.net/20.500.12258/19149 |
Appears in Collections: | Статьи, проиндексированные в SCOPUS, WOS |
Files in This Item:
File | Size | Format | |
---|---|---|---|
WoS 1365 .pdf Restricted Access | 1.69 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.