Title: Influence of the ceramic powder morphology and forming conditions on the optical transmittance of YAG:Yb ceramics
Authors: Malyavin, F. F.
Малявин, Ф. Ф.
Tarala, V. A.
Тарала, В. А.
Kravtsov, A. A.
Кравцов, А. А.
Chikulina, I. S.
Чикулина, И. С.
Shama, M. S.
Шама, М. С.
Medyanik, E. V.
Медяник, Е. В.
Ziryanov, V. S.
Зырянов, В. С.
Evtushenko, E. A.
Евтушенко, Е. А.
Vakalov, D. S.
Вакалов, Д. С.
Lapin, V. A.
Лапин, В. А.
Kuleshov, D. S.
Кулешов, Д. С.
Tarala, L. V.
Тарала, Л. В.
Mitrofanenko, L. M.
Митрофаненко, Л. М.
Keywords: Agglomeration coefficient;Cold isostatic pressing;Forming;Highly transparent YAG:Yb ceramics;Specific surface area;Pressing (forming)
Issue Date: 2019
Publisher: Elsevier Ltd
Citation: Malyavin, F.F., Tarala, V.A., Kuznetsov, S.V., Kravtsov, A.A., Chikulina, I.S., Shama, M.S., Medyanik, E.V., Ziryanov, V.S., Evtushenko, E.A., Vakalov, D.S., Lapin, V.A., Kuleshov, D.S., Tarala, L.V., Mitrofanenko, L.M. Influence of the ceramic powder morphology and forming conditions on the optical transmittance of YAG:Yb ceramics // Ceramics International. - 2019. - Volume 45. - Issue 4. - Pages 4418-4423
Series/Report no.: Ceramics International
Abstract: The influence of the dispersity and morphology of ceramic powders on the characteristics of green bodies and the optical transmittance of YAG:Yb (20 at%) ceramics was considered. The effect of the specific surface area on the relative density of compacts was studied. An increase in the specific surface area from 1.45 to 12.38 m2/g led to a decrease in the relative density of green body compacts from 52% to 38% under the fixed uniaxial pressure of 50 MPa. An increase in the uniaxial pressing value up to 150 MPa provided a maximum increase of the optical transmission of ceramics. However, an increase in the specific surface area and uniaxial pressure led to the appearance of macrodefects in ceramic samples. Cold isostatic pressing at 200 MPa after uniaxial pressing at 50 MPa resulted in an increase of optical transparency and the elimination of the macrodefect formation in ceramics. Dispersity and morphology of ceramic powders have a significant effect on the optical transparency of ceramics. Forming conditions had insignificant influence on optical characteristics. Highly transparent YAG:Yb ceramics with 80% transmittance were developed
URI: https://www.scopus.com/record/display.uri?eid=2-s2.0-85057172967&origin=resultslist&sort=plf-f&src=s&st1=Influence+of+the+ceramic+powder+morphology+and+forming+conditions+&st2=&sid=00517e04cd9db0cd4826521d40659860&sot=b&sdt=b&sl=81&s=TITLE-ABS-KEY%28Influence+of+the+ceramic+powder+morphology+and+forming+conditions+%29&relpos=1&citeCnt=2&searchTerm=
http://hdl.handle.net/20.500.12258/7094
Appears in Collections:Статьи, проиндексированные в SCOPUS, WOS

Files in This Item:
File Description SizeFormat 
scopusresults 640 .pdf959.95 kBAdobe PDFThumbnail
View/Open
WoS 544 .pdf105.61 kBAdobe PDFThumbnail
View/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.