Название: | The scandium impact on the sintering of YSAG:Yb ceramics with high optical transmittance |
Авторы: | Nikova, M. S. Никова, М. С. Tarala, V. A. Тарала, В. А. Malyavin, F. F. Малявин, Ф. Ф. Vakalov, D. S. Вакалов, Д. С. Lapin, V. A. Kuleshov, D. S. Кулешов, Д. С. Kravtsov, A. A. Кравцов, А. А. Chikulina, I. S. Чикулина, И. С. Tarala, L. V. Тарала, Л. В. Evtushenko, E. A. Евтушенко, Е. А. Medyanik, E. V. Медяник, Е. В. Krandievsky, S. O. Крандиевский, С. О. Лапин, В. А. |
Ключевые слова: | Garnets;Optical ceramics;Scandium;Vacuum sintering;YSAG:Yb;Ytterbium compounds |
Дата публикации: | 2021 |
Издатель: | Elsevier Ltd |
Библиографическое описание: | Nikova, M.S., Tarala, V.A., Malyavin, F.F., Vakalov, D.S., Lapin, V.A., Kuleshov, D.S., Kravtsov, A.A., Chikulina, I.S., Tarala, L.V., Evtushenko, E.A., Medyanik, E.V., Krandievsky, S.O., Bogach, A.V., Kuznetsov, S.V. The scandium impact on the sintering of YSAG:Yb ceramics with high optical transmittance // Ceramics International. - 2021. - Том: 47. - Выпуск: 2. - Стр.: 1772-1784 |
Источник: | Ceramics International |
Краткий осмотр (реферат): | Optical ceramics based on Yb2O3–Y2O3-Sc2O3–Al2O3 solid solutions with a garnet structure were obtained using chemical precipitation and vacuum sintering techniques. In the samples' composition, scandium was incorporated into both dodecahedral and octahedral garnet sites in ratios from 4: 1 to 1: 4. The differential thermal analysis and dilatometry methods were used to study the phase transformations kinetics of the precursor powders and the vacuum sintering kinetics of YSAG:Yb compacts. It was found that the garnet cationic composition has a strong effect on the optical ceramics' sintering temperature ranges. It was also pointed out that an increase in the scandium content in the dodecahedral YSAG:Yb garnet site was accompanied by a decrease in the vacuum sintering temperature, which ensures maximum compaction rate. For the samples with the Y2.15Yb0.25Sc1.00Al4.6O12, Y2.35Yb0.25Sc1.00Al4.4O12, Y2.55Yb0.25Sc1.00Al4.2O12, Y2.52Yb0.25Sc0.38Al4.85O12 compositions, optical transmission in visible and near-infrared range of more than 80% was achieved |
URI (Унифицированный идентификатор ресурса): | http://hdl.handle.net/20.500.12258/14199 |
Располагается в коллекциях: | Статьи, проиндексированные в SCOPUS, WOS |
Файлы этого ресурса:
Файл | Описание | Размер | Формат | |
---|---|---|---|---|
scopusresults 1393 .pdf Доступ ограничен | 10.53 MB | Adobe PDF | Просмотреть/Открыть | |
WoS 981 .pdf Доступ ограничен | 261.07 kB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.